| Alliage | Composition principale% | Densité (g / cm³) | Module d'élasticité (GPa) | Coefficient de dilatation thermique (×10-6/K) | Conductivité électrique (% IACS) | Conductivité thermique (W/(m²K)) | ||||||
| Cu | Cu+Zn | |||||||||||
| H70 | 68.5-71.5 | ≥ 99.7 | 8.53 | 105 | 19.7 | 26 | 120 | |||||
| Propriétés mécaniques | |||||||||||||||||||
| Alliage | Etat | Résistance à la tractionRm/Mpa | Élongation% | Dureté | |||||||||||||||
| GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB (HV) | JIS (haute tension) | ASTM(HR)Superficiel 30T | FR(HV) |
| H70 | C2600 | C26000 | CuZn30 | O60 | O | M20 | R270 | ≥ 290 | ≥ 275 | 285-350 | 270-350 | ≥ 40 | ≥ 35 | ≥ 40 | ≥ 40 | ≤ 90 | - | - | 55-90 |
| H01 | 1 / 4H | H01 | R350 | 325-410 | 325-420 | 340-405 | 350-430 | ≥ 35 | ≥ 30 | ≥ 34 | ≥ 21 | 85-115 | 75-125 | 43-57 | 95-125 | ||||
| H02 | 1 / 2H | H02 | R410 | 355-460 | 355-450 | 395-460 | 410-490 | ≥ 25 | ≥ 23 | ≥ 19 | ≥ 9 | 100-130 | 85-145 | 56-66 | 120-155 | ||||
| - | 3 / 4H | H03 | - | - | 375-490 | 440-510 | - | - | ≥ 10 | ≥ 8 | - | - | 95-160 | 65-70 | - | ||||
| H04 | H | H04 | R480 | 410-540 | 410-540 | 490-560 | ≥ 480 | ≥ 13 | - | ≥ 6 | - | 120-160 | 105-175 | 70-73 | ≥ 150 | ||||
| H06 | EH | H06 | 520-620 | 520-620 | 570-635 | ≥ 4 | - | ≥ 2 | 150-190 | 145-195 | 74-76 | ||||||||
| H08 | SH | H08 | ≥ 570 | 570-670 | 625-690 | - | - | ≥ 1 | ≥ 180 | 165-215 | 76-78 | ||||||||
| - | ESH | H10 | - | ≥ 620 | 655-715 | - | - | ≥ 1 | - | ≥ 180 | 77-79 | ||||||||