C64750 hutumiwa sana katika viunganisho vya umeme, muafaka wa kuongoza wa semiconductor, vituo, nk katika mifumo ya ishara na nguvu.
Daraja la | Muundo wa kemikali (%) ≤ | Unene (Mm) |
||||||||
ASTM | Cu | Fe | Zn | Ni | Si | Sn | Mg | P | Zr | |
C64750 | Mizani | 1.0 | 1.0 | 1.0-3.0 | 0.1-0.7 | 0.05-0.8 | 0.1 | 0.1 | 0.1 | 0.05-0.8 |
Mali ya kimwili | |||||
Wiani (g/cm³) |
Modulus ya elasticity (GPA) |
Mgawo wa upanuzi wa joto (×10-6/ K) |
Utaratibu wa umeme (%IACS) |
Conductivity ya joto W(m·K) |
|
8.7 | 130 | 17.1 | 40 | 165 | |
Mitambo mali | Bend mali | ||||
hasira | Mtihani wa mvutano | 90°R/T(Nene≤0.5mm) | |||
Tensile Nguvu (MPa) |
Nguvu za Mazao (MPa) |
Elongation % (A50) |
Njia nzuri | Njia mbaya | |
TM00 | 590-670 | ≥520 | ≥8 | 0 | 0 |
TM02 | 640-720 | ≥590 | ≥8 | 0 | 0 |
TM03 | 690-780 | ≥620 | ≥6 | 0 | 0.5 |
TM04 | 740-860 | ≥690 | ≥3 | 0.5 | 1 |