C52100 Utangulizi wa shaba ya fosforasi
Utendaji: Ductility bora, upinzani wa uchovu, na upinzani wa kutu
Inatumika sana katika utengenezaji wa chemchem mbali mbali za mawasiliano, viunga vya elektroniki, brashi za waya, na sehemu za kubadili, nk.
Inaweza kutumika kwa ajili ya kuzalisha bidhaa za ukanda wa shaba wa fosforasi iliyosagwa laini, yenye ukubwa wa nafaka ≤ 0.005mm.
Kwa sasa, C52100 (C5210/QSn8-0.3) imefanikiwa kuzalisha kwa wingi bidhaa za moto-dip (physical electroplating) na tabaka za bati za 1-6μm zinakubalika.
| Standard | Daraja la | Muundo wa Kemikali (%) ≤ | ||||||||||||||||
| Sn | Zn | Fe | Pb | Ni | P | nyingine | Cu | |||||||||||
| GB | QSn8-0.3 | 7.0-9.0 | 0.20 | 0.10 | 0.05 | - | 0.03-0.35 | 0.5 | Mizani | |||||||||
| EN | CuSn8 | 7.5-8.5 | 0.20 | 0.10 | 0.02 | 0.2 | 0.01-0.4 | 0.2 | Mizani | |||||||||
| ASTM | C52100 | 7.0-9.0 | 0.20 | 0.10 | 0.05 | - | 0.03-0.35 | - | Mizani | |||||||||
| JIS | C5210 | 7.0-9.0 | 0.20 | 0.10 | 0.02 | - | 0.03-0.35 | 0.5 | Mizani | |||||||||
| Mali ya Kimwili | ||||||||||||||||||
|
Wiani (G/Cm³) |
Modulus ya Elasticity (GPA) |
Upanuzi wa mafuta ya kutosha (×10-6/K) |
Hali ya Umeme (%IACS) |
Conducttivity ya joto W(M·K) |
||||||||||||||
| 8.8 | 110 | 18.5 | 11 | 67 | ||||||||||||||
| Mali ya Mitambo | ||||||||||||||||||
| Daraja la | Jimbo |
Tensile Nguvu Rm / MPa |
Kipengee A11.3/% |
Ugumu HV |
||||||||||||||
| GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | EN |
GB (HV) |
JIS (HV) |
ASTM (HR) |
EN (HV) |
| QSn8-0.3 | C5210 | C52100 | CuSn8 | O60 | O60 | R370/H090 | ≥345 | 365-460 | 370-450 | ≥45 | ≥50 | ≤120 | 20-70 | 90-120 | ||||
| H01 | R450/H135 | 390-510 | - | 450-550 | ≥40 | ≥20 | 100-160 | - | 135-175 | |||||||||
| H02 | 1 / 2H | H02 | R540/H170 | 490-610 | 470-610 | 475-580 | 540-630 | ≥30 | ≥27 | ≥13 | 150-205 | 140-205 | 69-91 | 170-200 | ||||
| H04 | H | H04 | R600/H190 | 590-705 | 590-705 | 585-690 | 600-690 | ≥12 | ≥20 | ≥50 | 180-235 | 185-235 | 89-97 | 190-220 | ||||
| H06 | EH | H06 | R660/H210 | 685-785 | 685-785 | 670-770 | 660-750 | ≥5 | ≥11 | ≥3 | 210-250 | 210-260 | 93-100 | 210-240 | ||||
| H08 | SH | H08 | R740/H230 | ≥735 | 735-835 | 725-820 | ≥740 | - | ≥9 | ≥2 | ≥230 | 230-270 | 95-102 | ≥230 | ||||
| - | ESH | H10 | - | - | 770-885 | 760-830 | - | - | ≥5 | - | - | 245-285 | 96-103 | - | ||||
Maswali
Swali: Muda wako wa kujifungua ni wa muda gani?
J: Kwa ujumla ni ndani ya siku 15 ikiwa bidhaa ziko kwenye hisa. au ni chini ya siku 30 ikiwa bidhaa hazipo, ni kulingana na wingi.
Swali: Je, unatoa sampuli?
J: Ndiyo, tunaweza kutoa sampuli
Swali: Masharti yako ya malipo ni yapi?
A.30% T/T mapema, salio kabla ya usafirishaji. Na bei inategemea nyenzo na wingi.
Ikiwa una swali lingine, tafadhali jisikie huru kuwasiliana nasi.