Kwa kuongeza Sn, Ni, na usio wa kiwango zinazofuata katika mradi wa chuma, C19025 inapitia nguvu ya kibigurio, upatikanaji mwingi, na uzinduzi mzuri wa streesu, pamoja na uzito mzuri. Inatumika katika vifaa vya motori, vikamati na zile zingine.
| Daraja | Mchanganyiko wa Kimia (% )≤ | Unene (mm) |
|||||
| ASTM | Cu | Sn | Ni | P | Zn | 0.05-5.0 | |
| C19025 | Mizani | 0.7-1.1 | 0.8-1.2 | 0.03-0.07 | ≤0.2 | ||
| Sifa za fisikali | |||||||
| wiani (g⁄cm³) |
Moduli ya Elasticity (GPa) |
Thermal Expansion Coefficient (×10-6/K) |
Uwanja wa Umoja (%IACS) |
Conductivity ya joto W(M·K) |
|||
| 8.9 | 130 | 17 | 40 | 161 | |||
| Majirani ya Mekaniki | Majirani ya Kuvaa | |||||
| Temper | Ugumu HV |
Mtihani wa Kupakama | 90°R/T(Thick≤0.5mm) | |||
| Nguvu ya Kuvuta Rm/MPa |
Ungano wa kuzaliwa MPa |
Ukong'era % |
Njia nzuri | Njia mbaya | ||
| H01 | 120-155 | 335-470 | 300-420 | ≥20 | 0 | 0 |
| H02 | 135-170 | 440-520 | 410-490 | ≥8 | 0 | 0 |
| H04 | 155-180 | 500-570 | 475-540 | ≥6 | 0 | 0 |
| H06 | 160-195 | 540-590 | 510-560 | ≥4 | 0 | 0.5 |
| H08 | 175-210 | 580-650 | 555-625 | ≥4 | - | - |
Majaribio ya studio inayotokana na uzoefu wa sasa, ndani na mapigano yasiyo ya kwanza kutoka mwanzo wetu.