Kuboresha la alai la C14415 Copper-tin
C14415——Alisi ya Cu-Sn, ina usimbaji sawa na chuma la kupong'aa, ina mifumo ya ngumu zaidi ya uwanja na upigishaji wa kifua, na inatumika kwa faida za kiwango cha msimu wa transistor (chips ya circuit ya kiungo cha nguvu), vijiti vya gari, vizuri za baridi, na viresi vya switch.
| Daraja | Ung'obeo (ki%) | Unene (mm) |
||||||
| GB | ASTM | JIS | EN | Cu | Sn | 0.08-3.5 | ||
| TSn0.12 | C14415 | C1441 | CuSn0.15 | 99.96 | 0.10-0.15 | |||
| Sifa za fisikali | ||||||||
| wiani (g⁄cm³) |
Moduli ya Elasticity (GPa) |
Thermal Expansion Coefficient (×10-6/K) |
Uwanja wa Umoja (%IACS) |
Conductivity ya joto W(M·K) |
||||
| 8.93 | 120 | 17.3 | 83 | 330 | ||||
| Majirani ya Mekaniki | Majirani ya Kuvaa | |||||||
| Temper | Ungofu wa Vickers (HV) |
Mtihani wa Kupakama | 90°R\/T (Kipepeo≤0.5mm) | |||||
| Nguvu ya Kuvuta (MPa) |
Ungano wa kuzaliwa (MPa) |
Ukong'era (%) |
Njia nzuri | Njia mbaya | ||||
| R300 | 85-110 | 300-370 | ≥250 | ≥4 | 0.0 | 0.0 | ||
| R360 | 110-130 | 360-430 | ≥300 | ≥3 | 0.0 | 0.0 | ||
| R420 | 120-150 | 420-490 | ≥350 | ≥3 | 1.0 | 1.0 | ||
| R460 | ≥130 | ≥460 | ≥410 | - | 0.5 | 2.0 | ||
Majaribio ya studio inayotokana na uzoefu wa sasa, ndani na mapigano yasiyo ya kwanza kutoka mwanzo wetu.