| Dukat | Kompożizzjoni Kimika (%)≤ | ||||||||||||||
| GB | ASTM | EN | Cu | Ni+Co | Fe | Mn | Pb | P | S | C | Mg | Si | Zn | Sn | oħra |
| BFe10-1-1 | C70600 | CuNi10 | Bilanċ | 9.0-11.0 | 1.0-1.5 | 0.5-1.0 | 0.02 | 0.006 | 0.01 | 0.05 | 0.15 | 0.3 | 0.03 | 0.7 | |
| Dukat | temper | Ebusija HV |
Test tat-tensjoni | |
| Tensile Rm / MPa |
Elongazzjoni % |
|||
| BFe10-1-1 | O60 | - | ≥275 | ≥25 |
| H04 | ≥370 | ≥3 | ||