C21000 C2100 CuZn5 H95 pajp tar-ram
C21000 C2100 CuZn5 H95 pajp tar-ram
C21000 C2100 CuZn5 H95 pajp tar-ram
C21000 C2100 CuZn5 H95 pajp tar-ram
C21000 C2100 CuZn5 H95 pajp tar-ram
C21000 C2100 CuZn5 H95 pajp tar-ram
C21000 C2100 CuZn5 H95 pajp tar-ram
C21000 C2100 CuZn5 H95 pajp tar-ram
C21000 C2100 CuZn5 H95 pajp tar-ram
C21000 C2100 CuZn5 H95 pajp tar-ram
C21000 C2100 CuZn5 H95 pajp tar-ram
C21000 C2100 CuZn5 H95 pajp tar-ram

C21000 C2100 CuZn5 H95 pajp tar-ram

  • introduzzjoni
introduzzjoni
Grad Kompożizzjoni Maġġuri% Densità (g/cm³) Modulu ta' elastiċità (GPa) Koeffiċjent ta' espansjoni termali (×10-6/K) Konduttività elettrika (%IACS) Konduttività termali (W/(m`K))
Cu Cu+Zn
H95 94.0-96.0 ≥99.8 8.86 115 18 54 243
propjetajiet mekkaniċi
Grad Membru Tensili StrengthRm/Mpa Titwil% Ebusija
GB JIS ASTM EN GB JIS ASTM EN GB JIS ASTM EN GB JIS ASTM EN GB(HV) JIS(HV) ASTM (HR) Superfiċjali 30T EN(HV)
H95 C2100 C21000 CuZn5 O60 O M20 R230 ≥215 ≥205 220-290 230-280 ≥30 ≥33 - ≥36 - - - 45-75
- 1 / 4H H01 R270 - 225-305 255-325 270-350 - ≥23 - ≥12 - - 34-51 75-110
- 1 / 2H H02 - - 265-345 290-355 - - ≥18 - - - - 46-57 -
- - H03 - - - 315-385 - - - - - - - 52-60 -
H04 H H04 R340 ≥320 ≥305 345-405 ≥340 ≥3 - - ≥4 - - 57-62 ≥110
- - H06 - - - 385-440 - - - - - - - 62-66 -
- - H08 - - - 415-470 - - - - - - - 64-68 -
- - H10 - - - 420-475 - - - - - - - 65-69 -

黄铜管详情页.jpg

Interessat fis-Servizzi Tagħna?

Prattika ta 'studjo ffukata fuq disinn modern, pajsaġġi interjuri mill-bidu tagħna.

Indirizz tagħna

  • Nru 1199, Yuanqu Road, Jiading District, Shanghai, iċ-Ċina
  • + 86-21 56610102
  • [email protected]

Ikseb Quote Ħieles

Ir-rappreżentant tagħna se jikkuntattjak dalwaqt.
email
isem
Isem tal-Kumpanija
messaġġ
0/1000