| Grad | Kompożizzjoni kimika （%）≤ | ||||||||
| GB | ASTM | JIS | Cu | Ni + Co. | Fe | Mn | Pb | P | S |
| B5 | - | - | Bilanċ | 4.5-5.5 | 0.02 | - | ≤ 0.7 | 0.01 | 0.01 |
| C | Mg | Si | Zn | Sn | oħrajn | ||||
| 0.03 | - | - | - | - | 0.5 | ||||
| propjetajiet mekkaniċi | ||||
| Grad | temper | Test tat-tensjoni | ||
| Tensile Rm / MPa |
Qawwa tar-Rendiment MPa |
Elongazzjoni % |
||
| B5 | O60 | ≥215 | - | ≥32 |
| H04 | ≥370 | - | ≥10 | |