| Dukat | Kompożizzjoni Kimika (%)≤ | ||||||||||||||
| GB | ASTM | EN | Cu | Ni+Co | Fe | Mn | Pb | P | S | C | Mg | Si | Zn | Sn | oħra |
| B19 | Bilanċ | 18-20 | 0.5 | 0.5 | 0.005 | 0.01 | 0.01 | 0.05 | 0.05 | 0.15 | 0.3 | 1.8 | |||
| Dukat | temper | Ħxuna | Ebusija HV |
Test tat-tensjoni | |
| Tensile Rm / MPa |
Elongazzjoni % |
||||
| B19 | O60 | ≤ 0.2 | - | ≥290 | ≥25 |
| H04 | ≥390 | ≥3 | |||