  • Introduction
Introduction

Cu NI Sn compositione modulata est stannum aeris roboratum, quae altam fortitudinem gerunt resistendi, et remissio accentus excellens resistentia. Eodem tempore etiam bene conductivity habet. Mixtura late adhibetur in fabricandis partium conductivis et obsistentibus sicut gestus, frutices, manicas gerentes, summus potentiae electronicarum partium, ac subtilitas obturaculum in terminales.

Grade Chemical composition%)≤ Crassitudo
(Mm)
ASTM Cu Sn Ni Mn other 0.05-5.0
C72700 Balance 5.5-6.5 8.5-9.5 0.05-0.3 ≤1.0
Spermatophyta
Densitas
(g/cm³)
Secundum modulum elasticitas
(GPa)
Scelerisque expansion coefficientes
(×10-6/K)
electrica conductivity
(%IACS)
Scelerisque conductivity
W(m·K)
8.89 130 17.1 12-14 -
mechanica proprietates, Flectere possessiones
temper duritiam
HV
Tensio test 90°R/T(Tick≤0.5mm)
Distrahentes fortitudo
Rm / MPa
cede virtus:
MPa
elongation
%
Bene via Malum iter
1 / 4H 145-220 510-620 ≥500 ≥16 0.5 0.5
1/4HT ≥300 ≥885 ≥750 ≥7 - -
1 / 2H 180-240 590-695 ≥500 ≥15 2 2
1/2HT ≥280 ≥930 ≥790 ≥6 - -
H 210-270 685-835 ≥580 ≥4 3 3
HT ≥300 ≥980 ≥830 ≥5 - -

FAQ

Q: Ut longo tempore partum est?

A: Generaliter intra 15 dies est si bona in stirpe sunt. vel minus quam XXX dies, si bona non sint, secundum quantitatem.

Q: Tu exempla praebes?

A: Immo specimen offerre potuimus

Q: Quid ls vestri termini solucionis

A.30% T/T in antecessum, statera ante amet. Et pretium attenditur secundum materiam et quantitatem
Si aliam quaestionem habes, placet liberum contactus nos.

1(5194accb8d).jpg

Interest in Our Services?

Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.

our Address

  • No. 1199, Yuanqu Road, Jiading District, Shanghai, China
  • + 86 21 56610102,
  • [email protected]

A Free Quote

Procurator noster mox te contact.
Email
nomine
nomen corporationis
Nuntius
0/1000