Elementis adiectis ut Ni, Si, Mg ad matrix aeris est typica senescit admiscendi corroboratio. C70250 vires altas, conductivity, et praecipitatio NiSi Phase facit stannum optimum accentus relaxationis resistentia. Adhiberi potest pro connectoribus autocinetis, tabulis plumbeis, connectoribus elasticis, etc.
| Grade | Chemical composition%）≤ | Crassitudo (Mm) |
||||||
| ASTM | EN | JIS | Cu | Ni | Si | Mg | Zn | 0.05-2.0 |
| C70250 | CuNi3SiMg | C7025 | Balance | 2.2-4.2 | 0.25-1.2 | 0.05-0.30 | ≤1.0 | |
| Spermatophyta | ||||||
| Densitas (g/cm³) |
Secundum modulum elasticitas (GPa) |
Scelerisque expansion coefficientes (×10-6/K) |
electrica conductivity (%IACS) |
Scelerisque conductivity W(m·K) |
||
| 8.8 | 130 | 17.6 | 45 | 190 | ||
| mechanica proprietates, | Flectere possessiones | |||||
| temper | duritiam HV |
Tensio test | 90°R/T(Crish＜0.5mm) | |||
| Distrahentes fortitudo Rm / MPa |
cede virtus: MPa |
elongation % |
Bene via | Malum iter | ||
| TM00 | 180-220 | 620-760 | ≥550 | ≥14 | 0.0 | 0.0 |
| TM02 | 190-240 | 655-780 | ≥585 | ≥8 | 0.5 | 0.5 |
| TM03 | 210-250 | 690-810 | ≥655 | ≥7 | 1.0 | 1.0 |
| TM04 | 220-270 | 760-850 | ≥720 | ≥2 | 1.5 | 1.5 |
| TM06 | 250-290 | 800-880 | ≥780 | ≥1 | 2.0 | 3.0 |
| TM08 | 270-330 | 840-920 | ≥810 | ≥1 | 2.5 | 3.0 |
| TM10 | 300-350 | 900-1000 | ≥880 | - | 3.5 | 4.0 |
FAQ
Q: Ut longo tempore partum est?
A: Generaliter intra 15 dies est si bona in stirpe sunt. vel minus quam XXX dies, si bona non sint, secundum quantitatem.
Q: Tu exempla praebes?
A: Immo specimen offerre potuimus
Q: Quid ls vestri termini solucionis
A.30% T/T in antecessum, statera ante amet. Et pretium attenditur secundum materiam et quantitatem
Si aliam quaestionem habes, placet liberum contactus nos.
Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.
EN