C52100 Introductio aenea Phosphorica
Euismod: Optima ductilis, lassitudo resistentia, corrosio resistentia
Late usus est in productione variorum contactuum fontium, contactorum electronicorum, virgultorum filum, partes commutandae, etc
Potest adhiberi ad phosphoro aeris detractam productis subtilibus granis producendis, cum magnitudine grani ≤ 0.005mm.
In praesenti, C52100 (C5210/QSn8-0.3) feliciter massam calidam-intingendam (electro-physicam) productam cum stratis plumbi 1-6μm acceptum est.
| Latin | Grade | Chemical composition%） ≤ | ||||||||||||||||
| Sn | Zn | Fe | Pb | Ni | P | other | Cu | |||||||||||
| GB | QSn8-0.3 | 7.0-9.0 | 0.20 | 0.10 | 0.05 | - | 0.03-0.35 | 0.5 | Balance | |||||||||
| EN | CuSn8 | 7.5-8.5 | 0.20 | 0.10 | 0.02 | 0.2 | 0.01-0.4 | 0.2 | Balance | |||||||||
| ASTM | C52100 | 7.0-9.0 | 0.20 | 0.10 | 0.05 | - | 0.03-0.35 | - | Balance | |||||||||
| JIS | C5210 | 7.0-9.0 | 0.20 | 0.10 | 0.02 | - | 0.03-0.35 | 0.5 | Balance | |||||||||
| Spermatophyta | ||||||||||||||||||
| Densitas (g/cm³) |
Secundum modulum elasticitas (GPa) |
Scelerisque expansion coefficientes (×10-6/K) |
electrica conductivity (%IACS) |
Scelerisque conductivity W(m·K) |
||||||||||||||
| 8.8 | 110 | 18.5 | 11 | 67 | ||||||||||||||
| mechanica proprietates, | ||||||||||||||||||
| Grade | rei publicae | Distrahentes fortitudo Rm / MPa |
elongation A11.3/% |
duritiam HV |
||||||||||||||
| GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | EN | GB (HV) |
JIS (HV) |
ASTM (HR) |
EN (HV) |
| QSn8-0.3 | C5210 | C52100 | CuSn8 | O60 | O60 | R370/H090 | ≥345 | 365-460 | 370-450 | ≥45 | ≥50 | ≤120 | 20-70 | 90-120 | ||||
| H01 | R450/H135 | 390-510 | - | 450-550 | ≥40 | ≥20 | 100-160 | - | 135-175 | |||||||||
| H02 | 1 / 2H | H02 | R540/H170 | 490-610 | 470-610 | 475-580 | 540-630 | ≥30 | ≥27 | ≥13 | 150-205 | 140-205 | 69-91 | 170-200 | ||||
| H04 | H | H04 | R600/H190 | 590-705 | 590-705 | 585-690 | 600-690 | ≥12 | ≥20 | ≥50 | 180-235 | 185-235 | 89-97 | 190-220 | ||||
| H06 | EH | H06 | R660/H210 | 685-785 | 685-785 | 670-770 | 660-750 | ≥5 | ≥11 | ≥3 | 210-250 | 210-260 | 93-100 | 210-240 | ||||
| H08 | SH | H08 | R740/H230 | ≥735 | 735-835 | 725-820 | ≥740 | - | ≥9 | ≥2 | ≥230 | 230-270 | 95-102 | ≥230 | ||||
| - | ESH | H10 | - | - | 770-885 | 760-830 | - | - | ≥5 | - | - | 245-285 | 96-103 | - | ||||
FAQ
Q: Quousque partus est tempus?
A: Generaliter intra 15 dies est si bona in stirpe sunt. vel minus quam XXX dies, si bona non sint, secundum quantitatem.
Q: Tu exempla praebes?
A: Immo specimen offerre potuimus
Q: Quid ls solucionis termini vestri?
A.30% T/T in antecessum, statera ante amet. Pretium autem attenditur secundum materiam et quantitatem.
Si aliam quaestionem habes, placet liberum contactus nos.