C51100 Introductio aenea Phosphorica
C51100 phosphoro aeneo stanneo cum contento Sn circiter 4.0%. Hoc mixturae altae elasticitates, vires, resistentiam gerunt, caliditas resistentia, accentus relaxatio resistentia, et corrosio resistentia. Adhiberi potest novas energiae vehiculi connexiones fabricare, terminales wiring, partes signare, connexiones elasticas, etc.
| Grade | Chemical composition%） | ||||||||
| GB | ASTM | JIS | STREPITUS | Cu | Fe | Pb | Sn | P | Zn |
| Qsn4.0-3.0 | C51100 | C5111 | CuSn4 | Balance | <0.1 | <0.05 | 3.5-4.9 | 0.03-0.35 | <0.3 |
| Spermatophyta | |||||||||
| Densitas (g/cm³) |
Secundum modulum elasticitas (GPa) |
Scelerisque expansion coefficientes (×10-6/K) |
electrica conductivity (%IACS) |
Scelerisque conductivity (W/(m·K)) |
|||||
| 8.86 | 115 | 17.2 | 20 | 83 | |||||
| mechanica proprietates, | Flectere possessiones | ||||||||
| temper | duritiam HV |
Tensio test | 180° R/T（Thick≤0.5mm） | ||||||
| Distrahentes fortitudo Rm / MPa |
cede virtus: MPa |
elongation % |
Bene via | Malum iter | |||||
| O60 | 75-120 | ≥295 | - | ≥45 | 0 | 0 | |||
| H01 | 80-150 | 345-440 | - | ≥30 | 0 | 0.5 | |||
| H02 | 120-180 | 410-510 | 340-460 | ≥17 | 0.5 | 1 | |||
| H04 | 150-200 | 490-590 | 420-560 | ≥12 | - | 2 | |||
| H06 | 170-220 | 570-660 | 500-630 | ≥6 | - | - | |||
FAQ
Q: Quousque partus est tempus?
A: Generaliter intra 15 dies est si bona in stirpe sunt. vel minus quam XXX dies, si bona non sint, secundum quantitatem.
Q: Tu exempla praebes?
A: Immo specimen offerre potuimus
Q: Quid ls solucionis termini vestri?
A.30% T/T in antecessum, statera ante amet. Et pretium attenditur secundum materiam et quantitatem
Si aliam quaestionem habes, placet liberum contactus nos.
Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.
EN