C51000 est phosphorus aeneus stannum cum 5.0% circiter stanneo. Hoc mixturae altae elasticitates, vires, resistentiam gerunt, caliditas resistentia, accentus relaxatio resistentia, et corrosio resistentia. Adhiberi potest novas energiae vehiculi connexiones fabricare, terminales wiring, partes signare, connexiones elasticas, etc.
| Grade | Chemical composition%） | |||||||
| GB | ASTM | STREPITUS | Cu | Fe | Pb | Sn | P | Zn |
| Qsn5-0.2 | C51000 | CuSn5 | Balance | <0.1 | <0.05 | 4.2-5.8 | 0.03-0.35 | <0.3 |
| Spermatophyta | |||||
| Densitas (g/cm³) |
Secundum modulum elasticitas (GPa) |
Scelerisque expansion coefficientes (×10-6/K) |
electrica conductivity (%IACS) |
Scelerisque conductivity (W/(m·K)) |
|
| 8.86 | 115 | 17.2 | 17 | 81 | |
| mechanica proprietates, | Flectere possessiones | |||||
| temper | duritiam HV |
Tensio test | 90°R/T（Thick≤0.5mm） | |||
| Distrahentes fortitudo Rm / MPa |
cede virtus: MPa |
elongation % |
Bene via | Malum iter | ||
| O60 | 80-120 | ≥305 | - | ≥45 | 0 | 0 |
| H01 | 90-160 | 370-470 | - | ≥30 | 0 | 0.5 |
| H02 | 130-190 | 470-570 | 400-500 | ≥18 | 0.5 | 1 |
| H04 | 170-220 | 570-665 | 500-630 | ≥10 | 1 | 2 |
| H06 | 190-230 | 620-710 | 570-680 | ≥7 | 1 | 3 |
| H08 | ≥200 | ≥660 | ≥630 | ≥5 | - | - |