| Grade | Chemical composition%） | Crassitudo (Mm) |
|||||
| GB | ASTM | JIS | Cu | Sn | P | Fe | 0.2-2.0 |
| - | C50715 | - | Balance | 1.7-2.3 | 0.025-0.04 | 0.05-0.15 | |
| Spermatophyta | |||||||
| Densitas (g/cm³) |
Secundum modulum elasticitas (GPa) |
Scelerisque expansion coefficientes (×10-6/K) |
electrica conductivity (%IACS) |
Scelerisque conductivity W(m·K) |
|||
| 8.9 | 121 | 17.6 | 32 | 160 | |||
| mechanica proprietates, | Flectere possessiones | ||||||
| temper | duritiam HV |
Tensio test | 90°R/T（Thick＜0.8mm） | ||||
| Distrahentes fortitudo Rm / MPa |
cede virtus: MPa |
elongation % |
Bene via | Malum iter | |||
| H02 | 120-165 | 395-500 | 295-415 | ≥16 | 0 | 0 | |
| H04 | 160-190 | 515-600 | 440-545 | ≥6 | 0 | 1 | |
| H06 | 170-200 | 550-625 | 490-570 | ≥5 | 0.5 | 1.5 | |
| H08 | ≥185 | 605-665 | 550-625 | ≥3 | - | - | |
FAQ
Q: Ut longo tempore partum est?
A: Generaliter intra 15 dies est si bona in stirpe sunt. vel minus quam XXX dies, si bona non sint, secundum quantitatem.
Q: Tu exempla praebes?
A: Immo specimen offerre potuimus
Q: Quid ls vestri termini solucionis
A.30% T/T in antecessum, statera ante amet. Et pretium attenditur secundum materiam et quantitatem
Si aliam quaestionem habes, placet liberum contactus nos.
Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.
EN