C19025 Product introduction
Sn, Ni, et alia elementa matricis aeneae vestigium addens, C19025 exhibet altam vim, elasticitatem, et excellentem vim relaxationis effectus, necnon optimam conductivity. applicatur ad terminales autocineticos, connexiones, etc.
| Grade | Chemical composition%）≤ | Crassitudo (Mm) |
|||||
| ASTM | Cu | Sn | Ni | P | Zn | 0.05-5.0 | |
| C19025 | Balance | 0.7-1.1 | 0.8-1.2 | 0.03-0.07 | ≤0.2 | ||
| Spermatophyta | |||||||
| Densitas (g/cm³) |
Secundum modulum elasticitas (GPa) |
Scelerisque expansion coefficientes (×10-6/K) |
electrica conductivity (%IACS) |
Scelerisque conductivity W(m·K) |
|||
| 8.9 | 130 | 17 | 40 | 161 | |||
| mechanica proprietates, | Flectere possessiones | ||||||
| temper | duritiam HV |
Tensio test | 90°R/T(Tick≤0.5mm) | ||||
| Distrahentes fortitudo Rm / MPa |
cede virtus: MPa |
elongation % |
Bene via | Malum iter | |||
| H01 | 120-155 | 335-470 | 300-420 | ≥20 | 0 | 0 | |
| H02 | 135-170 | 440-520 | 410-490 | ≥8 | 0 | 0 | |
| H04 | 155-180 | 500-570 | 475-540 | ≥6 | 0 | 0 | |
| H06 | 160-195 | 540-590 | 510-560 | ≥4 | 0 | 0.5 | |
| H08 | 175-210 | 580-650 | 555-625 | ≥4 | - | - | |
+