C19000 Alloy introduction
Addendo Ni, P, et alia elementa matricis aeneae vestigium, C19000 exhibet vires altas, elasticitatem, optimam conductivity, accentus relaxationem resistentiam, resistentiam vis corrosionis. Late usus est in connexione terminalium, tabularum plumbearum, iungentium autocinetorum et aliorum camporum.
| Grade | Chemical composition%）≤ | Crassitudo (Mm) |
|||||
| GB | ASTM | EN | Cu | Ni | P | Zn | 0.08-5.0 |
| TNi1.1-0.25 | C19000 | CUNi1P | Balance | 0.9-1.3 | 0.15-0.35 | <0.8 | |
| Spermatophyta | |||||||
| Densitas (g/cm³) |
Secundum modulum elasticitas (GPa) |
Scelerisque expansion coefficientes (×10-6/K) |
electrica conductivity (%IACS) |
Scelerisque conductivity W(m·K) |
|||
| 8.88 | 130 | 17.6 | 64 | 253 | |||
| mechanica proprietates, | Flectere possessiones | ||||||
| temper | duritiam HV |
Tensio test | 90°R/T(Tick≤0.5mm) | ||||
| Distrahentes fortitudo Rm / MPa |
cede virtus: MPa |
elongation % |
Bene via | Malum iter | |||
| TM00 | 165-200 | 530-620 | 500-600 | ≥8 | 0.5 | 1.0 | |
| TM02 | 175-210 | 580-650 | 560-640 | ≥4 | 0.5 | 1.3 | |
| TM04 | 180-220 | 620-720 | 600-710 | ≥2 | 1.0 | 1.7 | |
FAQ
Q: Ut longo tempore partum est?
A: Generaliter intra 15 dies est si bona in stirpe sunt. vel minus quam XXX dies, si bona non sint, secundum quantitatem.
Q: Tu exempla praebes?
A: Immo specimen offerre potuimus.
Q: Quid ls solucionis termini vestri?
A.30% T/T in antecessum, statera ante amet. Pretium autem attenditur secundum materiam et quantitatem.
Si aliam quaestionem habes, placet liberum contactus nos.
Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.
LA