  • Introduction
Introduction

Addens Mg, P, et alia elementa matricis aeneae vestigium dat C18665 altam vim, elasticitatem, optimam conductivity, accentus relaxationis resistentiam, resistentiam vis corrosionis. C18665 adhiberi possunt ad materias fabricandas ut terminales automotives, contactus motus nullos, fontes contactus, busbars, ruptores ambitus, pugnae terminales, fuses, etc.

Grade Chemical composition%)≤ Crassitudo
(Mm)
EN GB ASTM Cu Mg P
CuMgP TMg0.5 C18665 ≥99.0 0.4-0.9 0.002-0.04 0.08-5.0
Spermatophyta
Densitas
(g/cm³)
Secundum modulum elasticitas
(GPa)
Scelerisque expansion coefficientes
(×10-6/K)
electrica conductivity
(%IACS)
Scelerisque conductivity
W(m·K)
8.8 125 17.3 60 253
mechanica proprietates, Flectere possessiones
temper duritiam
HV
Tensio test 90°R/T(Crish<0.5mm)
Distrahentes fortitudo
Rm / MPa
cede virtus:
MPa
elongation
%
Bene via Malum iter
H01 90-140 365-450 300-410 ≥15 0 0
H02 120-170 420-510 370-480 ≥10 0 0
H04 150-190 480-570 440-550 ≥7 0 0.5
H06 170-210 540-630 490-620 ≥5 0 1
H08 ≥180 ≥590 ≥540 - - -

FAQ

Q: Ut longo tempore partum est?

A: Generaliter intra 15 dies est si bona in stirpe sunt. vel minus quam XXX dies, si bona non sint, secundum quantitatem.

Q: Tu exempla praebes?

A: Immo specimen offerre potuimus

Q: Quid ls vestri termini solucionis

A.30% T/T in antecessum, statera ante amet. Et pretium attenditur secundum materiam et quantitatem
Si aliam quaestionem habes, placet liberum contactus nos.

1(5194accb8d).jpg

Interest in Our Services?

Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.

our Address

  • No. 1199, Yuanqu Road, Jiading District, Shanghai, China
  • + 86 21 56610102,
  • [email protected]

A Free Quote

Procurator noster mox te contact.
Email
nomine
nomen corporationis
Nuntius
0/1000