| Kelas | Komposisi Utama% | Densitas (g / cm³) | Modulus elastisitas (GPa) | Koefisien ekspansi termal (×10-6/K) | Konduktivitas listrik (%IACS) | Konduktivitas termal (W/(m`K)) | ||||||
| Cu | Cu+Zn | |||||||||||
| H68 | 67.0-70.0 | ≥ 99.7 | 8.53 | 105 | 20 | 26 | 123 | |||||
| Peralatan mekanis | |||||||||||||||||||
| Kelas | perangai | Kekuatan TarikRm/Mpa | Pemanjangan% | Kekerasan | |||||||||||||||
| GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB(HV) | JIS (HV) | ASTM(HR)Superfisial 30T | ID(HV) |
| H68 | CuZn33 | O60 | - | - | R280 | ≥ 290 | - | - | 280-360 | ≥ 40 | - | - | ≥ 40 | ≤ 90 | - | - | 55-90 | ||
| H01 | - | - | R350 | 325-410 | - | - | 350-430 | ≥ 35 | - | - | ≥ 23 | 85-115 | - | - | 95-125 | ||||
| H02 | - | - | - | 355-460 | - | - | - | ≥ 25 | - | - | - | 100-130 | - | - | - | ||||
| H04 | - | - | R420 | 410-540 | - | - | 420-500 | ≥ 13 | - | - | ≥ 6 | 120-160 | - | - | 125-155 | ||||
| H06 | - | - | R500 | 520-620 | - | - | ≥ 500 | ≥ 4 | - | - | - | 150-190 | - | - | ≥ 155 | ||||
| H08 | - | - | ≥ 570 | - | - | - | - | - | - | ≥ 180 | - | - | |||||||