| Kelas | Komposisi Utama % |
Kepadatan (g / cm³) |
Modulus elastisitas (IPK) |
Koefisien ekspansi termal (×10-6/ K) |
Konduktivitas listrik (%IACS) |
konduktivitas termal (W/(m·K)) |
||||||
| 铜Cu | Tembaga + Tembaga Cu + Zn | |||||||||||
| H85 | 84.0-86.0 | ≥ 99.8 | 8.75 | 115 | 18.5 | 35 | 159 | |||||
| Peralatan mekanis | |||||||||||||||||||
| Kelas | Negara | Kekuatan tarik RM/Mpa |
pemanjangan % |
Kekerasan | |||||||||||||||
| GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB (Tinggi V) |
JIS (Tinggi V) |
ASTM (SDM) Superfisial 30T |
EN (Tinggi V) |
| H85 | C2300 | C23000 | CuZn15 | O60 | O | M20 | R260 | ≥ 260 | ≥ 245 | 255-325 | 260-310 | ≥ 40 | ≥ 40 | ≥ 43 | ≥ 36 | ≤ 85 | - | - | 55-85 |
| H02 | 1 / 4H | H01 | R300 | 305-380 | 275-355 | 305-370 | 300-370 | ≥ 15 | ≥ 28 | ≥ 15 | ≥ 16 | 80-115 | - | 42-57 | 85-115 | ||||
| H04 | 1 / 2H | H02 | R350 | ≥ 350 | 305-380 | 350-420 | 350-420 | - | ≥ 23 | ≥ 8 | ≥ 4 | ≥ 105 | - | 56-64 | 105-135 | ||||
| H | R410 | ≥ 355 | ≥ 410 | - | - | ≥ 125 | |||||||||||||
| - | - | H03 | - | - | - | 395-460 | - | - | - | ≥ 4 | - | - | - | 63-68 | - | ||||
| - | - | H04 | - | - | - | 435-495 | - | - | - | ≥ 4 | - | - | - | 67-71 | - | ||||
| - | - | H06 | - | - | - | 495-550 | - | - | - | ≥ 3 | - | - | - | 70-74 | - | ||||
| - | - | H08 | - | - | - | 540-595 | - | - | - | ≥ 3 | - | - | - | 74-76 | - | ||||
| - | - | H10 | - | - | - | 565-620 | - | - | - | ≥ 2 | - | - | - | 75-77 | - | ||||