| Kelas | Komposisi Utama% | Densitas (g / cm³) | Modulus elastisitas (GPa) | Koefisien ekspansi termal (×10-6/K) | Konduktivitas listrik (%IACS) | Konduktivitas termal (W/(m`K)) | ||||||
| Cu | Cu+Zn | |||||||||||
| H95 | 94.0-96.0 | ≥ 99.8 | 8.86 | 115 | 18 | 54 | 243 | |||||
| Peralatan mekanis | |||||||||||||||||||
| Kelas | Negara | Kekuatan TarikRm/Mpa | Pemanjangan% | Kekerasan | |||||||||||||||
| GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB(HV) | JIS (HV) | ASTM(HR)Superfisial 30T | ID(HV) |
| H95 | C2100 | C21000 | CuZn5 | O60 | O | M20 | R230 | ≥ 215 | ≥ 205 | 220-290 | 230-280 | ≥ 30 | ≥ 33 | - | ≥ 36 | - | - | - | 45-75 |
| - | 1 / 4H | H01 | R270 | - | 225-305 | 255-325 | 270-350 | - | ≥ 23 | - | ≥ 12 | - | - | 34-51 | 75-110 | ||||
| - | 1 / 2H | H02 | - | - | 265-345 | 290-355 | - | - | ≥ 18 | - | - | - | - | 46-57 | - | ||||
| - | - | H03 | - | - | - | 315-385 | - | - | - | - | - | - | - | 52-60 | - | ||||
| H04 | H | H04 | R340 | ≥ 320 | ≥ 305 | 345-405 | ≥ 340 | ≥ 3 | - | - | ≥ 4 | - | - | 57-62 | ≥ 110 | ||||
| - | - | H06 | - | - | - | 385-440 | - | - | - | - | - | - | - | 62-66 | - | ||||
| - | - | H08 | - | - | - | 415-470 | - | - | - | - | - | - | - | 64-68 | - | ||||
| - | - | H10 | - | - | - | 420-475 | - | - | - | - | - | - | - | 65-69 | - | ||||