C51900 fosforbronsi tutvustus
C51900 on kuprini-tiin-fosforligne, mis on kõrge korroosioonitugevusega, väsimustugevusega, magneetsete omaduste vastu tugev, lihtne brasdeerimine ja hea töötlemise omadused. Seda materjali kasutatakse laialdaselt täpsete seadmete ja mõõdikute elastsete komponentide, kulase ja antimagneetsete osade tootmiseks. C51900 sobib ka veined fosfor-kupriiniliste lehttoodete tootmiseks. Ja C51900 (C5191/QSn6.5-0.1) on edukalt massitoodetud kuivatud (füüsiline elektroplaatimine) tooteid, millel on 1-6μm tiini kiht.
| Hinne | Keemiline koostis (%)≥ Mikroelement (%)≤ | |||||||||||||||||
| Sn | Al | Zn | Fe | Pb | Ni | p | muud | Cu | ||||||||||
| GB | QSn6.5-0.1 | 6.0-7.0 | 0.002 | 0.3 | 0.05 | 0.02 | 0.10-0.25 | 0.4 | TASAKAALUSTATUD | |||||||||
| EN | CuSn6 | 5.5-7.0 | 0.2 | 0.1 | 0.02 | 0.2 | 0,01-0,4 | 0.2 | TASAKAALUSTATUD | |||||||||
| ASTM | C51900 | 5.0-7.0 | - | 0.30 | 0.10 | 0.05 | - | 0,03-0,35 | - | TASAKAALUSTATUD | ||||||||
| JIS | C5191 | 5.5-7.0 | - | 0.2 | 0.1 | 0.02 | - | 0,03-0,35 | 0.5 | TASAKAALUSTATUD | ||||||||
| Füüsikalised omadused | ||||||||||||||||||
| Tihedus (G/Cm³) |
Jõhkrutusmoodul (GPa) |
Termline laienemiskordaja (×10-6/K) |
Elektrikandlikkus (%IACS) |
Termiline juhtivus (W/(M·K)) |
||||||||||||||
| 8.86 | 118 | 17.2 | 13 | 75 | ||||||||||||||
| Hinne | olek | Lahutusjõud Rm\/MPa |
Pikkendumine A11.3/% |
Kõvadus HV |
||||||||||||||
| GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | EN | GB (HV) |
JIS (HV) |
ASTM (HR) |
EN (HV) |
| QSn6.5-0.1 | C5191 | C51900 | CuSn6 | O60 | O | O60 | R350/H080 | ≥315 | ≥315 | 330-435 | 350-420 | ≥40 | ≥42 | ≥45 | ≤120 | - | 18-66 | 80-110 |
| H01 | 1⁄4H | - | R420/H125 | 390-510 | 390-510 | - | 420-520 | ≥35 | ≥35 | ≥17 | 110-155 | 100-160 | - | 125-165 | ||||
| H02 | 1⁄2H | H02 | R500/H160 | 490-610 | 490-610 | 440-545 | 500-590 | ≥10 | ≥20 | ≥8 | 150-190 | 150-205 | 65-88 | 160-190 | ||||
| H04 | H | H04 | R560/H180 | 590-690 | 590-685 | 550-680 | 560-650 | ≥8 | ≥8 | ≥5 | 180-230 | 180-230 | 86-95 | 180-210 | ||||
| H06 | EH | - | R640/H200 | 635-720 | 635-720 | - | 640-730 | ≥5 | ≥5 | ≥3 | 200-240 | 200-240 | - | 200-230 | ||||
| H08 | SH | - | R720/H220 | ≥690 | ≥690 | - | ≥720 | - | - | - | ≥210 | ≥210 | - | ≥220 | ||||