Avaleht / Tooteid / Kaas / messintorud
| Hinne | Peamine koostis % |
Tihedus (G/Cm³) |
Jõhkrutusmoodul (GPa) |
Termline laienemiskordaja (×10 -6/K) |
Elektrikandlikkus (%IACS) |
Termiline juhtivus (W/(M·K)) |
||||||
| Cu | Cu+Zn | |||||||||||
| H63 | 62.0-65.0 | ≥99.7 | 8.43 | 105 | 20.2 | 23 | 120 | |||||
| Mehaanilised omadused | |||||||||||||||||||
| Hinne | olek | Lahutusjõud Rm\/MPa |
Pikkendumine % |
Kõvadus | |||||||||||||||
| GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB (HV) |
JIS (HV) |
ASTM (HR) Pind 30T |
EN (HV) |
| H63 | C2720 | C27200 | CuZn37 | O60 | O | M20 | R300 | ≥290 | ≥275 | 285-350 | 300-370 | ≥35 | ≥40 | - | ≥38 | ≤95 | - | - | 55-95 |
| - | 1⁄4H | H01 | - | - | 325-410 | 340-405 | - | - | ≥35 | - | - | - | 75-125 | 43-57 | - | ||||
| H02 | 1⁄2H | H02 | R350 | 350-470 | 355-440 | 385-455 | 350-440 | ≥20 | ≥28 | - | ≥19 | 90-130 | 85-145 | 54-67 | 95-125 | ||||
| - | - | H03 | R410 | - | - | 435-505 | 410-490 | - | - | - | ≥8 | - | - | 64-70 | 120-155 | ||||
| H04 | H | H04 | R480 | 410-630 | ≥410 | 485-550 | 480-560 | ≥10 | - | - | ≥3 | 125-165 | ≥105 | 67-72 | 150-180 | ||||
| H06 | - | H06 | R550 | ≥585 | - | 560-625 | ≥550 | ≥2,5 | - | - | - | ≥155 | - | 71-75 | ≥170 | ||||