C19210 Product introduction
C19210 is a typical aging precipitation strengthening alloy with excellent conductivity and thermal conductivity; It also has moderate strength, good bending performance, as well as good corrosion resistance and electroplating performance; It is commonly used for connector pins, lead frames, electrical industrial components, air conditioning heat exchanger pipes, etc.
| Grade | Chemical composition（%）≤ | |||||||
| GB | ASTM | JIS | Cu | Fe | P | Thickness (mm) |
||
| TFe0.1 | C19210 | C1921 | Balance | 0.05-0.15 | 0.025-0.04 | 0.08-4.0 | ||
| Physical properties | ||||||||
| Density (g/cm³) |
Modulus of elasticity (GPa) |
Thermal expansion coefficient (×10-6/K) |
Electrical conductivity (%IACS) |
Thermal conductivity W(m·K) |
||||
| 8.91 | 115 | 17 | 85 | 350 | ||||
| Mechanical properties | Bend properties | |||||||
| Temper | Hardness HV |
Electrical conductivity (%IACS) |
Tension test | 90°R/T(Thick＜0.8mm) | 180°R/T(Thick＜0.8mm) | |||
| Tensile Strength Rm/MPa |
Elongation A11.3 % |
Good way | Bad way | Good way | Bad way | |||
| O60 | ≤100 | ≥85 | 260-330 | ≥30 | 0.0 | 0.0 | 0.0 | 0.0 |
| H01 | 90-115 | ≥85 | 300-360 | ≥20 | 0.0 | 0.0 | 1.5 | 1.5 |
| H02 | 100-125 | ≥85 | 320-410 | ≥6 | 1.0 | 1.0 | 1.5 | 2.0 |
| H03 | 110-130 | ≥85 | 360-440 | ≥5 | 1.5 | 1.5 | 2.0 | 2.0 |
| H04 | 115-135 | ≥85 | 390-470 | ≥4 | 2.0 | 2.0 | 2.0 | 2.0 |
| H06 | ≥130 | ≥85 | ≥430 | ≥2 | 2.5 | 2.5 | 2.5 | 3.0 |
| H06S | ≥125 | ≥90 | ≥420 | ≥3 | 2.5 | 2.5 | 2.5 | 3.0 |
| H08 | 130-155 | ≥85 | 440-510 | ≥1 | 3.0 | 4.0 | 3.0 | 4.0 |
| H10 | ≥135 | ≥85 | ≥450 | ≥1 | - | - | - | - |
FAQ
Q: How long is your delivery time?
A: Generally it is within 15 days if the goods are in stock. or it is less than 30 days if the goods are not in stock, it is according to quantity.
Q: Do you provide samples ?
A: Yes, we could offer the sample
Q: What ls your terms of payment ?
A.30% T/T in advance ,balance before shipment. And the price depends on the material and the quantity
If you have another question, please feel free to contact us.
Studio practice focused on modern design, interiors landscapes from our inception.
EN